In this paper, the great sensitivity and selectivity to NO2 detection at low temperature down to ppb-level of zinc oxide (ZnO) thick-film sensors are reported. Sensor performances of ZnO films prepared by screen printing technique were evaluated comparing two different ZnO nano-powders in wurtzite crystal structure. Powders were synthetized by hydrothermal route (HT-ZnO) and by auto combustion sol-gel synthesis (AC-ZnO). After proper characterization of the nanopowders, the thick film sensors were fabricated by screen-printing technique onto α-alumina substrates equipped with Pt interdigitated electrodes, followed by a thermal treatment. The sensor response was studied in the range 50 – 250 °C. Best results were reached at 150 °C, with sensor response R (Zg/Z0) - defined as the ratio between impedance under NO2 (Zg) and impedance under dry air (Z0) - equal to 42.92 for HT-ZnO and to 23.18 for AC-ZnO under 0.5 ppm of NO2 in dry conditions. Finally, response and recovery time were measured, and selectivity of the sensors was determined by exposing the film toward O3, CO2, CH4, N2O and humidity at the best working temperature. Both sensors showed great sensitivity for NO2 detection, supporting the exploitation of these sensors as NO2 detectors at ppb level.

ZnO thick films for NO2 detection: effect of different nanostructures on the sensors’ performances / Ziegler, Daniele; Marchisio, Andrea; Palmero, Paola; Pugliese, Diego; Cauda, Valentina; Tulliani, Jean-Marc. - In: JOURNAL OF MATERIALS SCIENCE. MATERIALS IN ELECTRONICS. - ISSN 0957-4522. - 30:24(2019), pp. 20958-20969. [10.1007/s10854-019-02463-x]

ZnO thick films for NO2 detection: effect of different nanostructures on the sensors’ performances

Diego Pugliese;
2019

Abstract

In this paper, the great sensitivity and selectivity to NO2 detection at low temperature down to ppb-level of zinc oxide (ZnO) thick-film sensors are reported. Sensor performances of ZnO films prepared by screen printing technique were evaluated comparing two different ZnO nano-powders in wurtzite crystal structure. Powders were synthetized by hydrothermal route (HT-ZnO) and by auto combustion sol-gel synthesis (AC-ZnO). After proper characterization of the nanopowders, the thick film sensors were fabricated by screen-printing technique onto α-alumina substrates equipped with Pt interdigitated electrodes, followed by a thermal treatment. The sensor response was studied in the range 50 – 250 °C. Best results were reached at 150 °C, with sensor response R (Zg/Z0) - defined as the ratio between impedance under NO2 (Zg) and impedance under dry air (Z0) - equal to 42.92 for HT-ZnO and to 23.18 for AC-ZnO under 0.5 ppm of NO2 in dry conditions. Finally, response and recovery time were measured, and selectivity of the sensors was determined by exposing the film toward O3, CO2, CH4, N2O and humidity at the best working temperature. Both sensors showed great sensitivity for NO2 detection, supporting the exploitation of these sensors as NO2 detectors at ppb level.
File in questo prodotto:
File Dimensione Formato  
ZnO thick films for NO2 detection_Effect of different nanostructures on the sensors’ performances.pdf

non disponibili

Tipologia: final published article (publisher’s version)
Licenza: Non Pubblico - Accesso privato/ristretto
Dimensione 1.87 MB
Formato Adobe PDF
1.87 MB Adobe PDF   Visualizza/Apri   Richiedi una copia
ZnO Pugliese.pdf

Open Access dal 16/11/2020

Tipologia: accepted manuscript (author’s post-print)
Licenza: Pubblico - Tutti i diritti riservati
Dimensione 1.48 MB
Formato Adobe PDF
1.48 MB Adobe PDF Visualizza/Apri

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11696/77311
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 5
  • ???jsp.display-item.citation.isi??? 5
social impact