We report on combined photoconductivity and annealing experiments in whisker-like crystals of the Bi-Sr-Ca-Cu-O (BSCCO) high-T-c superconductor. Both single-phase Bi2Sr2CaCu2O8+delta (Bi-2212) samples and crystals of the mixed phases Bi2Sr2Ca2Cu3O10+x (Bi-2223)/Bi-2212 have been subjected to annealing treatments at 90 degrees C in air in a few hours steps, up to a maximum total annealing time of 47 h. At every step, samples have been characterized by means of electrical resistance versus temperature (R versus T) and resistance versus time at fixed temperature (R versus t) measurements, both in the dark and under illumination with a UV-Vis halogen arc lamp. A careful comparison of the results from the two techniques has shown that, while for single-phase samples no effect is recorded, for mixed-phase samples an enhancement in the conductivity that increases with increasing annealing time is induced by the light at the nominal temperature T = 100 K, i.e. at an intermediate temperature between the critical temperatures of the two phases. A simple pseudo-1D model based on the Kudinov's scheme (Kudinov et al, 1993 Phys. Rev. B 47 9017-28) has been developed to account for the observed effects, which is based on the existence of Bi-2223 filaments embedded in the Bi-2212 matrix and on the presence of electronically active defects at their interfaces. This model reproduces fairly well the photoconductive experimental results and shows that the length of the Bi-2223 filaments decreases and the number of defects increases with increasing annealing time.

Photoconductivity effects in mixed-phase BSCCO whiskers / Truccato, M.; Imbraguglio, D.; Agostino, A.; Cagliero, S.; Pagliero, A.; Motzkau, H.; Rydh, A.. - In: SUPERCONDUCTOR SCIENCE & TECHNOLOGY. - ISSN 0953-2048. - 25:10(2012), p. 105010. [10.1088/0953-2048/25/10/105010]

Photoconductivity effects in mixed-phase BSCCO whiskers

Imbraguglio, D.;
2012

Abstract

We report on combined photoconductivity and annealing experiments in whisker-like crystals of the Bi-Sr-Ca-Cu-O (BSCCO) high-T-c superconductor. Both single-phase Bi2Sr2CaCu2O8+delta (Bi-2212) samples and crystals of the mixed phases Bi2Sr2Ca2Cu3O10+x (Bi-2223)/Bi-2212 have been subjected to annealing treatments at 90 degrees C in air in a few hours steps, up to a maximum total annealing time of 47 h. At every step, samples have been characterized by means of electrical resistance versus temperature (R versus T) and resistance versus time at fixed temperature (R versus t) measurements, both in the dark and under illumination with a UV-Vis halogen arc lamp. A careful comparison of the results from the two techniques has shown that, while for single-phase samples no effect is recorded, for mixed-phase samples an enhancement in the conductivity that increases with increasing annealing time is induced by the light at the nominal temperature T = 100 K, i.e. at an intermediate temperature between the critical temperatures of the two phases. A simple pseudo-1D model based on the Kudinov's scheme (Kudinov et al, 1993 Phys. Rev. B 47 9017-28) has been developed to account for the observed effects, which is based on the existence of Bi-2223 filaments embedded in the Bi-2212 matrix and on the presence of electronically active defects at their interfaces. This model reproduces fairly well the photoconductive experimental results and shows that the length of the Bi-2223 filaments decreases and the number of defects increases with increasing annealing time.
File in questo prodotto:
File Dimensione Formato  
Truccato_2012_Supercond._Sci._Technol._25_105010.pdf

non disponibili

Tipologia: final published article (publisher’s version)
Licenza: Non Pubblico - Accesso privato/ristretto
Dimensione 1.42 MB
Formato Adobe PDF
1.42 MB Adobe PDF   Visualizza/Apri   Richiedi una copia
1211.6594.pdf

accesso aperto

Tipologia: accepted manuscript (author’s post-print)
Licenza: Creative Commons
Dimensione 1.94 MB
Formato Adobe PDF
1.94 MB Adobe PDF Visualizza/Apri

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11696/64351
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 4
  • ???jsp.display-item.citation.isi??? 4
social impact