The control of the self-assembly (SA) process and nanostructure orientation in diblock copolymer (DBC) thick films is a crucial technological issue. Perpendicular orientation of the nanostructures in symmetric and asymmetric poly(styrene)-b-poly(methyl methacrylate) (PS-b-PMMA) block copolymer films obtained by means of simple thermal treatments was demonstrated to occur in well-defined thickness windows featuring modest maximum values, thus resulting in low aspect ratio (h/d < 2) of the final lithographic mask. In this manuscript, the thickness window corresponding to the perpendicular orientation of the cylindrical structures in asymmetric DBC is investigated at high temperatures (190 °C ≤ T ≤ 310 °C) using a rapid thermal processing machine. A systematic study of the annealing conditions (temperature and time) of asymmetric PS-b-PMMA (Mn = 67.1, polydispersity index = 1.09) films, with thicknesses ranging from 10 to 400 nm, allowed ordered patterns, with a maximum value of orientational correlation length of 350 nm, to be obtained for film thicknesses up to 200 nm. The complete propagation of the cylindrical structures through the whole film thickness in a high aspect ratio PS template (h/d ≈ 7) is probed by lift-off process. Si nanopillars are obtained having the same lateral ordering and characteristic dimensions of the DBC lithographic mask as further confirmed by grazing-incidence small-angle X-ray scattering experiments.

High aspect ratio PS-b-PMMA block copolymer masks for lithographic applications / Ferrarese Lupi, F; Giammaria, T J; Volpe, F G; Lotto, F; Seguini, G; Pivac, B; Laus, M; Perego, M. - In: ACS APPLIED MATERIALS & INTERFACES. - ISSN 1944-8244. - 6:23(2014), pp. 21389-96-21396. [10.1021/am506391n]

High aspect ratio PS-b-PMMA block copolymer masks for lithographic applications

Ferrarese Lupi, F
;
2014

Abstract

The control of the self-assembly (SA) process and nanostructure orientation in diblock copolymer (DBC) thick films is a crucial technological issue. Perpendicular orientation of the nanostructures in symmetric and asymmetric poly(styrene)-b-poly(methyl methacrylate) (PS-b-PMMA) block copolymer films obtained by means of simple thermal treatments was demonstrated to occur in well-defined thickness windows featuring modest maximum values, thus resulting in low aspect ratio (h/d < 2) of the final lithographic mask. In this manuscript, the thickness window corresponding to the perpendicular orientation of the cylindrical structures in asymmetric DBC is investigated at high temperatures (190 °C ≤ T ≤ 310 °C) using a rapid thermal processing machine. A systematic study of the annealing conditions (temperature and time) of asymmetric PS-b-PMMA (Mn = 67.1, polydispersity index = 1.09) films, with thicknesses ranging from 10 to 400 nm, allowed ordered patterns, with a maximum value of orientational correlation length of 350 nm, to be obtained for film thicknesses up to 200 nm. The complete propagation of the cylindrical structures through the whole film thickness in a high aspect ratio PS template (h/d ≈ 7) is probed by lift-off process. Si nanopillars are obtained having the same lateral ordering and characteristic dimensions of the DBC lithographic mask as further confirmed by grazing-incidence small-angle X-ray scattering experiments.
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11696/56953
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 32
  • ???jsp.display-item.citation.isi??? 32
social impact