In this paper the experimental results of tensile properties and indentation properties, as a function of pyramidal and spherical indenters, of Copper-Chromium-Zirconium alloy, in the macro-scale range at room temperature, are presented and compared. Measurements are performed on three Cu-Cr-Zr samples in order to evaluate different heat treatments: two samples are aged for 2 hours in a vacuum furnace at 480 °C, 550 °C and one sample is kept as received. The experimental procedures for the measurement of indentation modulus, by using the primary hardness standard machine at INRiM, and tensile modulus, by means of engineering tensile tests at CIRA, are described.